Перевод названия: Гидродинамическое диспергирование кальций-алюмосиликатных материалов из техногенного и нерудного сырья
Тип публикации: статья из журнала
Год издания: 2014
Ключевые слова: Hydrodynamic dispersion, cavitation, crystal ceramic foam, porous glass material, гидродинамическое диспергирование, кавитация, пористая стеклокерамика, зола, пеноматериал
Аннотация: Physicochemical properties of two calcium aluminosilicate materials after reducing in the hydrodynamic rotary generator in supercavitation mode were studied. The samples are the crystal ceramic foam based on Kansko-Achinsk lignite-ash and the porous glass material obtained from low-manganese nonmetallic feed. X-ray phase analysis, Показать полностьюEPR-method, NPR-method (the Mossbauer Effect) and optical microscopy were used. It was found that the material is changing its stucrure in a hydrodynamic dispersion process caused by high-cavitation. The nature of the changes depends on its initial state. Изучены физико-химические свойства двух кальций-алюмосиликатных материалов после измельчения в гидродинамическом генераторе роторного типа в режиме суперкавитации. Исследованы образцы - кристаллическая пенокерамика на основе зол бурых Канско-Ачинских углей и пористый стекломатериал, полученный из нерудного сырья с низким содержанием марганца. Для анализа были использованы методы РФА, ЭМР, ЯГР (эффект Мёссбауэра), оптическая микроскопия. Показано, что в процессе гидродинамического диспергирования за счет высокоэнергетического кавитационного воздействия в материалах происходят глубокие структурные изменения. Получено, что характер изменений зависит от исходного состояния исследуемого материала.
Журнал: Journal of Siberian Federal University. Серия: Техника и технологии
Выпуск журнала: Т. 7, № 1
Номера страниц: 3-12
ISSN журнала: 1999494X
Место издания: Красноярск
Издатель: Федеральное государственное автономное образовательное учреждение высшего образования Сибирский федеральный университет