Tuning of the Interparticle interactions in ultrafine ferrihydrite nanoparticles : научное издание

Описание

Тип публикации: статья из журнала

Год издания: 2022

Идентификатор DOI: 10.12989/anr.2022.12.6.605

Ключевые слова: ferrihydrite ultrafine nanoparticles, hyperfine structure, interparticle interactions, iron oxyhydroxide, superparamagnetic relaxation, surface coatings

Аннотация: We prepared two samples of ultrafine ferrihydrite (FH) nanoparticle ensembles of quite a different origin. First is the biosynthesized sample (as a product of the vital activity of bacteria Klebsiella oxytoca (hereinafter marked as FH-bact) with a natural organic coating and negligible magnetic interparticle interactions. And the sПоказать полностьюecond one is the chemically synthesized ferrihydrite (hereinafter FH-chem) without any coating and high level of the interparticle interactions. The interparticle magnetic interactions have been tuned by modifying the nanoparticle surface in both samples. The coating of the FH-bact sample has been partially removed by annealing at 150°C for 24 h (hereinafter FH-annealed). The FH-chem sample, vice versa, has been coated (1.0 g) with biocompatible polysaccharide (arabinogalactan) in an ultrasonic bath for 10 min (hereinafter FH-coated). The changes in the surface properties of nanoparticles have been controlled by XPS. According to the electron microscopy data, the modification of the nanoparticle surface does not drastically change the particle shape and size. A change in the average nanoparticle size in sample FH-annealed to 3.3 nm relative to the value in the other samples (2.6 nm) has only been observed. The estimated particle coating thickness is about 0.2‒0.3 nm for samples FH-bact and FH-coated and 0.1 nm for sample FH- annealed. Mössbauer and magnetization measurements are definitely shown that the drastic change in the blocking temperature is caused by the interparticle interactions. The experimental temperature dependences of the hyperfine field <Нhf>(Т) for samples FH-bact and FH-coated have not revealed the effect of interparticle interactions. Otherwise, the interparticle interaction energy Eint estimated from the <Нhf>(Т) for samples FH-chem and FH-annealed has been found to be 121kB and 259kB, respectively.?

Ссылки на полный текст

Издание

Журнал: Advances in Nano Research

Выпуск журнала: Т.12, 6

Номера страниц: 605-616

ISSN журнала: 2287237X

Персоны

  • Knyazev Yuriy V. (Kirensky Institute of Physics, Federal Research Center KSC SB RAS)
  • Balaev Dmitry A. (Siberian Federal University)
  • Yaroslavtsev Roman N. (Siberian Federal University)
  • Krasikov Aleksandr A. (Kirensky Institute of Physics, Federal Research Center KSC SB RAS)
  • Velikanov Dmitry A. (Kirensky Institute of Physics, Federal Research Center KSC SB RAS)
  • Mikhlin Yuriy L. (Institute of Chemistry and Chemical Technology, Federal Research Center KSC SB RAS)
  • Volochaev Mikhail N. (Kirensky Institute of Physics, Federal Research Center KSC SB RAS)
  • Bayukov Oleg A. (Kirensky Institute of Physics, Federal Research Center KSC SB RAS)
  • Stolyar Sergei V. (Siberian Federal University)
  • Iskhakov Rauf S. (Kirensky Institute of Physics, Federal Research Center KSC SB RAS)

Вхождение в базы данных