Тип публикации: статья из журнала
Год издания: 2022
Идентификатор DOI: 10.17516/1997-1397-2022-15-4-493-499
Ключевые слова: thin lms, solid-state synthesis, Cu6Sn5 intermetallic, η ↔ η′ reversible polymorphic transformations, тонкие плёнки, твердофазный синтез, интерметаллид Cu6Sn5, обратимый фазовый переход η ↔ η, thin films, η ↔ η′ reversible polymorphic trans-formations
Аннотация: The study results of solid-state synthesis of the Cu6Sn5 intermetallic in the Sn/Cu thin-lm systems during vacuum annealing from room temperature to 300 ◦C are presented. The initiation and nishing temperatures of the solid-state reaction between the Cu and Sn nanolayers and the phase composition of the reaction products were deterПоказать полностьюmined. The synthesized thin lms were monophasic andconsisted of the hexagonal η-Cu6Sn5 phase. It is assumed that the initiation temperature of the solid-state reaction in Sn/Cu thin lms is associated with the start temperature of the reverse polymorphic transformation η′ → η between the monoclinic and hexagonal Cu6Sn5 phases. Приведены результаты исследований твердофазного синтеза интерметаллида Cu6Sn5 в тонкопленочной системе Sn/Cu при отжиге в вакууме от комнатной температуры до 300 ◦C. Определены температуры начала и окончания твердофазной реакции между нанослоями Cu и Sn, а также фазовый состав продуктов реакции. Синтезированные тонкие пленки были однофазнымии состояли из гексагональной фазы η-Cu6Sn5. Сделано предположение, что температура начала твердофазной реакции в тонких пленках Sn/Cu связана с температурой начала обратного полиморфного превращения η′ → η между моноклинной и гексагональной фазами Cu6Sn5. The study results of solid-state synthesis of the Cu6Sn5 intermetallic in the Sn/Cu thin-film systems during vacuum annealing from room temperature to 300 °C are presented. The initiation and finishing temperatures of the solid-state reaction between the Cu and Sn nanolayers and the phase composition of the reaction products were determined. The synthesized thin films were monophasic and consisted of the hexagonal η-Cu6Sn5 phase. It is assumed that the initiation temperature of the solid-state reaction in Sn/Cu thin films is associated with the start temperature of the reverse polymorphic transformation η′ → η between the monoclinic and hexagonal Cu6Sn5 phases. © Siberian Federal University. All rights reserved.
Журнал: Журнал Сибирского федерального университета. Серия: Математика и физика
Выпуск журнала: Т. 15, № 4
Номера страниц: 493-499
ISSN журнала: 19971397
Место издания: Красноярск
Издатель: Сибирский федеральный университет