Перевод названия: Влияние состояния TiO 2 на окислительную делигнификацию древесины осины и соломы пшеницы
Тип публикации: статья из журнала
Год издания: 2014
Ключевые слова: TiO 2 catalyst, Oxidative delignification, Aspen wood, straw wheat, hydrogen peroxide, cellulose, катализатор TiO 2, окислительная делигнификация, древесина осины, солома пшеницы, пероксид водорода, целлюлоза
Аннотация: The in?uence of preparation methods on structural characteristics of TiO 2 catalysts was studied by the XRD, SEM, BET, DTA-DSC, FTIR techniques. Catalytic activity of obtained titanium dioxide samples was compared in reaction of oxidative deligni?cation of aspen wood and wheat straw by hydrogen peroxide in acetic acid- water mediumПоказать полностью. The use of titanium dioxide in rutile modi?cation allows to produce a cellulose product with lower content of a residual lignin, as compared to TiO 2 in anatase modi?cation. The increase of surface area of the TiO2 catalyst reduces its activity in wood and wheat straw deligni? cation. Методами РФА, СЭМ, БЭТ, ДТА-ДСК, ИКС изучено влияние способов получения катализаторов TiO 2 на их структурные характеристики. Сопоставлена каталитическая активность полученных образцов диоксида титана в реакции окислительной делигнификации древесины осины и соломы пшеницы пероксидом водорода в среде « уксусная кислота-вода ». Использование диоксида титана в модификации рутил позволяет получить целлюлозный продукт с более низким содержанием остаточного лигнина, чем при использовании TiO 2 в модификации анатаз. Увеличение удельной поверхности катализатора приводит к уменьшению степени делигнификации древесины осины и соломы пшеницы.
Журнал: Journal of Siberian Federal University. Серия: Химия
Выпуск журнала: Т. 7, № 3
Номера страниц: 316-325
ISSN журнала: 19982836
Место издания: Красноярск
Издатель: Федеральное государственное автономное образовательное учреждение высшего образования Сибирский федеральный университет